首页  >  覆铜板  >  详情
H1170

特性/ Features

Tg≥170℃ DSC                

优良耐CAF              Excellent Anti-CAF resistance 

优良的通孔可靠性           Excellent T/H reliability                      

Z轴热膨胀系数           Low Z-CTE 2.9%

优异的耐热性Td =347℃T288=30min   High thermal performance Td =347℃ ,T288=30min

 

应用领域/ Applications 

适合于高多层PCB、计算机及外围设备、通讯设备、汽车电子。

Suitable for high-count layer PCB, computer, communication equipment, Automotive electronics,

 

主要特性 / General properties

检测项目

Item               

单位

Unit

检测条件

Test Condition

规范值

Spec

典型值

Typical Value

玻璃化转变温度Tg

DSC

≥170

182

剥离强度 1oz Peel   Strength

N/mm

288℃, 10S

≥1.05

1.41

热应力

Thermal   stress

S

288℃,solder   dip

10

180 s                         No delamination

弯曲强度                                    Flexural   Strength

N/mm2

经向 LW

≥415

570

纬向CW

≥345

465

燃烧性Flammability

E 24/125

UL94V-0

V-0

表面电阻Surface   Resistivity

After   moisture

≥1.0×104

9.8×107

体积电阻Volume   Resistivity

MΩ·cm

After   moisture

≥1.0×106

3.21×108

介电常数

Dielectric Constant

1 MHZ

C 24/23/50

≤5.4

4.7

介质损耗角正切

Loss Tangent

1 MHZ

C 24/23/50

≤0.035

0.016

耐电弧Arc   Resistance

S

 D48/50D0.5/23

≥60

122

击穿电压

Dielectric  Breakdown 

KV

 D48/50D0.5/23

≥40

58

吸水率Moisture   Absorption

%

D24/23

≤0.35

0.10

热分解温度Td

Weight Loss   5%

≥340

360

CTE                                       Z-axis

Alpha 1

ppm / ℃

 

TMA

≤60

45

Alpha 2

ppm / ℃

≤300

270

50 - 260 ℃

%

≤3.0

2.9

T288

min

TMA

≥15

60

T300

min

TMA

≥2

20

相比漏电起痕指数 CTI                    

V

IEC-60112

175250

200

Specimen Thickness : 1.6mm ;   Specification sheetIPC-4101D/126is for your reference only

Explanation: C: Humidity conditioning;         D: Immersion conditioning in distilled water ;

           E: Temperature conditioning ;

半固化片介绍-H1170/ Prepreg instruction

H1170 P UV Prepreg):

prepreg   type

Resin   Content(%)

压合厚度Cured thickness(mm/mil)

R/C(%)含量

公差Tolerance

Nominal

Range(±)mil

%

±

mm

mil

mm

mil

7628HRC

52

2

0.234

9.21

0.022

0.9

50

2

0.223

8.78

0.022

0.9

48

2

0.212

8.35

0.02

0.8

7628

45

2

0.197

7.76

0.019

0.8

43

2

0.188

7.40

0.018

0.7

1506

50

2

0.173

6.81

0.017

0.7

48

2

0.166

6.54

0.017

0.7

2116

60

2

0.145

5.70

0.015

0.6

58

2

0.138

5.43

0.014

0.5

55

2

0.127

5.00

0.013

0.5

53

2

0.120

4.72

0.011

0.5

1080

68

2

0.087

3.43

0.008

0.3

65

2

0.077

3.03

0.008

0.3

63

2

0.074

2.91

0.008

0.3

106

75

2

0.058

2.30

0.006

0.2

73

2

0.053

2.10

0.005

0.2

71

2

0.048

1.90

0.005

0.2

 

 

建议压制程式: Suggest cycle

 a447d1655ae187fe72b75e48bcf0e7d3.png


储存条件温度≤23℃、湿度≤50%,保存时间3个月;温度≤5℃、密封条件下,保存时间6个月.

Storage Condition: T≤23℃& ≤50%RH,Within 3 months;  T≤5 ℃ Within 6 months (seal condition).

在上述要求内,我司可立即安排PP送样;若有特殊要求,由供需双方商定。Follow above condition,

Our company will arrange sample immediately. We can discuss if you have special requirement.